Soğuk Şekillendirme İşlemine Uygun Düşük Karbonlu Çinko ile Kaplanmış (Galvanize) Çelikler
البدائللا يوجد بديل لهذه الورقة.
Flat / Galvanised
Galvanized flat steel is manufactured by zinc-coating both sides of cold rolled metal by hot-dipping process. After having coated the steel surface with zinc, the coating of the interface is transformed into an alloy of iron-zinc layer through heating by induction and the galvannealed steel is produced.
Soğuk Şekillendirme İşlemine Uygun Düşük Karbonlu Çinko ile Kaplanmış (Galvanize) Çelikler
التركيب الكيميائي (%)
| المعيار المكافئ | رقم جودة إرديمير | Cmin. | Cmax. | Mnmax. | Pmax. | Smax. | Crmax. | Momax. | Nimax. | Vmax. | Nbmax. | Timax. | Cumax. | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| المعيار | جودة | |||||||||||||
| ASTM A653-2025 | CS Type B | 1306 | 0.02 | 0.15 | 0.60 | 0.03 | 0.035 | 0.15 | 0.06 | 0.20 | 0.008 | 0.008 | 0.025 | 0.25 |
- The limitation requests for the residual elements (Cu, Ni, Cr, Mo) which are not mentioned on the table are subjected to negotitation for special application purposes.
- Mn content is not specified in SAE standard. In ERDEMIR Mn content is aimed to minimum 0.20
الخواص الميكانيكية
| المعيار المكافئ | رقم جودة إرديمير | Re [N/mm2] | A(%) min. | |
|---|---|---|---|---|
| المعيار | جودة | |||
| A80 | ||||
| ASTM A653-2025 | CS Type B | 1306 | 205-380 | 20 |
- Yield strenght are measured in the longitudinal direction.
- Tensile test values apply to "longitudinal" test pieces
- Mechanical properties specified in the table are reference values only for guidance.