1660 جودة مواصفات الورقة
Galvanized,dual-phase steel with high yield strength for cold forming
البدائللا يوجد بديل لهذه الورقة.
Flat / Galvanised
Galvanized flat steel is manufactured by zinc-coating both sides of cold rolled metal by hot-dipping process. After having coated the steel surface with zinc, the coating of the interface is transformed into an alloy of iron-zinc layer through heating by induction and the galvannealed steel is produced.
Galvanized,dual-phase steel with high yield strength for cold forming
التركيب الكيميائي (%)
| المعيار المكافئ | رقم جودة إرديمير | Cmax. | Mnmax. | Pmax. | Smax. | Simax. | Almin. | Almax. | Vmax. | Bmax. | Cr+Momax. | Nb+Timax. | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| المعيار | جودة | ||||||||||||
| EN 10346:2015 | HCT590X+Z | 1660 | 0.15 | 2.50 | 0.04 | 0.015 | 0.75 | 0.015 | 1.50 | 0.20 | 50.00 | 1.40 | 0.15 |
- There are no chemical footnotes.
الخواص الميكانيكية
| المعيار المكافئ | رقم جودة إرديمير | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | n10-UE | BH2 [N/mm2] min. | ||
|---|---|---|---|---|---|---|---|---|
| المعيار | جودة | |||||||
| A800.4≤t≤0.59 | A800.6≤t≤2 | min. | ||||||
| EN 10346:2015 | HCT590X+Z | 1660 | 330-430 | 590 min. | 18 | 20 | 0.14 | 30 |
- The mechanical properties are valid for a period of 3 months from the date on which the products are made available.
- Tensile test values apply to "longitudinal" test pieces