Hot rolled unalloyed structural steels for manufacture of construction equipment, machines and various machine parts, general construction plates, road and railway vehicles
البدائللا يوجد بديل لهذه الورقة.
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Hot rolled unalloyed structural steels for manufacture of construction equipment, machines and various machine parts, general construction plates, road and railway vehicles
- Copper content shall be min 0.20% when Cu steel is specified.
- The lower limit of 'Si' does not apply in case the chemical composition of 'Al' in the steel is min 0.020%.
- Tensile test values apply to "transverse" test pieces
Flat / Plate
Heavy plate products are obtained by rolling semi-finished products with a rectangular cross-section (slab) produced by the continuous casting method to a specific temperature, with thicknesses ranging from 6.00 to 200.00 mm and widths ranging from 1000 to 3600 mm.
Hot rolled unalloyed structural steels for manufacture of construction equipment, machines and various machine parts, general construction plates, road and railway vehicles
- Copper content shall be min 0.20% when Cu steel is specified.
- The lower limit of 'Si' does not apply in case the chemical composition of 'Al' in the steel is min 0.020%.
- Silicon content shall be 0.15-0.40 % for thickness greater than 40 mm.
- Tensile test values apply to "transverse" test pieces