Zinc coated (galvanized) low carbon steels for cold forming
البدائللا يوجد بديل لهذه الورقة.
Flat / Galvanised
Galvanized flat steel is manufactured by zinc-coating both sides of cold rolled metal by hot-dipping process. After having coated the steel surface with zinc, the coating of the interface is transformed into an alloy of iron-zinc layer through heating by induction and the galvannealed steel is produced.
Zinc coated (galvanized) low carbon steels for cold forming
التركيب الكيميائي (%)
| المعيار المكافئ | رقم جودة إرديمير | Cmax. | Mnmax. | Pmax. | Smax. | Simax. | Almin. | Nbmax. | Timax. | |
|---|---|---|---|---|---|---|---|---|---|---|
| المعيار | جودة | |||||||||
| 52806/9.52873 | FEP05-ZNT/F/2S | 327 | 0.008 | 0.30 | 0.025 | 0.02 | 0.03 | 0.02 | 0.035 | 0.09 |
- The Al value which is specified in the table is the limit of the customer's specifications. The other limits are specified as reference value according to Erdemir manufacturing practice.
الخواص الميكانيكية
| المعيار المكافئ | رقم جودة إرديمير | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | n90 | r90 | ||
|---|---|---|---|---|---|---|---|---|
| المعيار | جودة | |||||||
| A800.4≤t≤0.69 | A800.7≤t≤2 | min. | ||||||
| 52806/9.52873 | FEP05-ZNT/F/2S | 327 | 140-180 | 270-330 | 38 | 40 | 0.2 | 1.9 min. |
- Tensile test values apply to "transverse" test pieces
- The mechanical properties are valid for a period of 6 months from the date on which the products are made available.