Hot rolled unalloyed structural steels for manufacture of construction equipment, machines and various machine parts, general construction plates, road and railway vehicles

البدائللا يوجد بديل لهذه الورقة.

Flat / Hot Rolled

Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.

Hot rolled unalloyed structural steels for manufacture of construction equipment, machines and various machine parts, general construction plates, road and railway vehicles

التركيب الكيميائي (%)

المعيار المكافئرقم جودة إرديميرCmax.Mnmax.Pmax.Smax.Simax.Cumax.CEmax.
المعيارجودة
EN 10025-2:2019S235J2+N CTA42390.171.400.0250.0250.030.550.35
  1. Carbon equivalent, CEV (IIW) % = C + Mn / 6 + (Cr + Mo + V) / 5 + (Ni + Cu) / 15
  2. Suitable for galvanizing as "Category A". Category A contains Si ≤ 0.030% and Si+2.5P ≤ 0.090%.
  3. Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.

الخواص الميكانيكية

المعيار المكافئرقم جودة إرديميرRe [N/mm2] t(thickness, mm)Rm [N/mm2]A(%) min. t(thickness, mm)Impact
المعيارجودة
A801.39≤t≤1.5A801.51≤t≤2A802.01≤t≤2.5A802.51≤t≤2.99A53≤t≤25Temperature ( ° C)6≤t≤7.49KVC J min.6≤t≤7.49Temperature ( ° C)7.5≤t≤9.99KVC J min.7.5≤t≤9.99Temperature ( ° C)10≤t≤25KVC J min.10≤t≤25
EN 10025-2:2019S235J2+N CTA4239225 min.235 min.360-5101617181924-2014-2021-2027
  1. Tensile test values apply to "transverse" test pieces
  2. Impact test is not carried out for thickness thinner than 6 mm.