813 جودة مواصفات الورقة
Soğuk Şekillendirme İşlemlerine Uygun Orta ve Yüksek Mukavemetli Düşük Alaşımlı, Özellikle Şasi, Güvenlik Bariyeri, Römork, Vinç Yapımında Kullanılan Çelikler
البدائللا يوجد بديل لهذه الورقة.
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Soğuk Şekillendirme İşlemlerine Uygun Orta ve Yüksek Mukavemetli Düşük Alaşımlı, Özellikle Şasi, Güvenlik Bariyeri, Römork, Vinç Yapımında Kullanılan Çelikler
التركيب الكيميائي (%)
| المعيار المكافئ | رقم جودة إرديمير | Cmax. | Mnmax. | Pmax. | Smax. | Simax. | Almin. | Nbmin. | Nbmax. | |
|---|---|---|---|---|---|---|---|---|---|---|
| المعيار | جودة | |||||||||
| 52812 | FEE 340 | 813 | 0.12 | 1.50 | 0.03 | 0.03 | 0.50 | 0.015 | 0.015 | 0.04 |
- (Nb + V + Ti) ≤ 0.20%
- Grade specified on the table, is produced within the framework of agreements with customers.
الخواص الميكانيكية
| المعيار المكافئ | رقم جودة إرديمير | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | Bend (Transverse , BMD) t: thickness | ||
|---|---|---|---|---|---|---|---|
| المعيار | جودة | ||||||
| A802≤t≤2.99 | A53≤t≤22 | 180° | |||||
| 52812 | FEE 340 | 813 | 340-420 | 410 min. | 23 | 23 | Ø 0,5 |
- Tensile test values apply to "longitudinal" test pieces
- The bending test is carried out only when specified at the time of enquiry and order.