6035 جودة مواصفات الورقة
Katlamaya Uygun Yapı Çelikleri
البدائللا يوجد بديل لهذه الورقة.
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Katlamaya Uygun Yapı Çelikleri
التركيب الكيميائي (%)
| المعيار المكافئ | رقم جودة إرديمير | Cmax. | Mnmax. | Pmax. | Smax. | Crmax. | Momax. | Nimax. | Vmax. | Nbmax. | Timax. | Cumax. | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| المعيار | جودة | ||||||||||||
| ASTM A1011-2025 | SS 36 Type 2 | 6035 | 0.25 | 1.35 | 0.035 | 0.04 | 0.15 | 0.06 | 0.20 | 0.008 | 0.008 | 0.025 | 0.20 |
- Titanium is permitted at the producer’s option, to the lesser of 3.4N + 1.5S or 0.025 %.
- When copper is requested in the chemical compositon, value specified in the table will be evaluated as minimum value. When copper is not specified, the copper limit is a maximum requirement.
- For each reduction of 0.01 percentage point below the specified max C an increase of 0.06 percentage point above the specified max for Mn is permitted up to a max of 1.50% by heat analysis
- Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.
الخواص الميكانيكية
| المعيار المكافئ | رقم جودة إرديمير | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | Bend (Transverse , BMD) t: thickness | |||
|---|---|---|---|---|---|---|---|---|
| المعيار | جودة | |||||||
| A2001.61≤t≤20 | A501.61≤t≤2.5 | A502.51≤t≤20 | 180° | |||||
| ASTM A1011-2025 | SS 36 Type 2 | 6035 | 250 min. | 400-550 | 16 | 20 | 21 | R 2d |
- The bending test is carried out only when specified at the time of enquiry and order.
- Tensile test values apply to "longitudinal" test pieces