6053 جودة مواصفات الورقة
High-strength structural steels for manufacture of any kind of machines and machine parts, general construction, road and railway vehicles
البدائللا يوجد بديل لهذه الورقة.
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
High-strength structural steels for manufacture of any kind of machines and machine parts, general construction, road and railway vehicles
التركيب الكيميائي (%)
| المعيار المكافئ | رقم جودة إرديمير | Cmin. | Cmax. | Mnmin. | Mnmax. | Pmax. | Smax. | Simin. | Simax. | Nbmin. | CEmax. | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| المعيار | جودة | |||||||||||
| EN 10025-2:2019 | S355J2C+N Mod1 | 6053 | 0.20 | 0.24 | 1.20 | 1.60 | 0.025 | 0.02 | 0.10 | 0.30 | 0.01 | 0.49 |
- This quality is produced as "Mod" within the framework of the agreements made with the customer
- Max carbon equivalent (CE) is increased by 0.01 % for Si ≤ 0.25%, and 0.02 % for Si ≤ 0.04 %
- Carbon equivalent, CEV (IIW) % = C + Mn / 6 + (Cr + Mo + V) / 5 + (Ni + Cu) / 15
- Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.
الخواص الميكانيكية
| المعيار المكافئ | رقم جودة إرديمير | Re [N/mm2] | Rm [N/mm2] t(thickness, mm) | A(%) min. t(thickness, mm) | Impact | Bend (Transverse , BMD) t: thickness | ||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| المعيار | جودة | |||||||||||||||||||||||||
| 1.8≤t≤2.99 | 3≤t≤20 | A801.8≤t≤2 | A802.01≤t≤2.5 | A802.51≤t≤2.99 | A53≤t≤20 | Temperature ( ° C)6≤t≤7.49 | KVC J min.6≤t≤7.49 | Temperature ( ° C)7.5≤t≤9.99 | KVC J min.7.5≤t≤9.99 | Temperature ( ° C)10≤t≤20 | KVC J min.10≤t≤20 | 90°1.8≤t≤2.5 | 90°2.51≤t≤3 | 90°3.01≤t≤4 | 90°4.01≤t≤5 | 90°5.01≤t≤6 | 90°6.01≤t≤7 | 90°7.01≤t≤8 | 90°8.01≤t≤10 | 90°10.01≤t≤12 | 90°12.01≤t≤14 | 90°14.01≤t≤16 | ||||
| EN 10025-2:2019 | S355J2C+N Mod1 | 6053 | 355 min. | 510-680 | 470-680 | 14 | 15 | 16 | 20 | -20 | 14 | -20 | 21 | -20 | 27 | R 4,0 mm | R 5,0 mm | R 6,0 mm | R 8,0 mm | R 10,0 mm | R 12,0 mm | R 16,0 mm | R 20,0 mm | R 25,0 mm | R 32,0 mm | R 36,0 mm |
- Tensile test values apply to "transverse" test pieces
- Impact test is not carried out for thickness thinner than 6 mm.
- Produced by normalizing or rolling equivalent to normalizing, and mechanical values after normalizing are guaranteed.
- The values are applicable for bend angles ≤90o