Low-carbon unalloyed mild steels for cold reducing with the obligation of batch annealing
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Low-carbon unalloyed mild steels for cold reducing with the obligation of batch annealing
- Mechanical test is not carried out.
- The limitation requests for the residual elements (Cu, Ni, Cr, Mo) which are not mentioned on the table are subjected to negotitation for special application purposes.
- Suitable for batch annealing after cold reducing.
- Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.
- Tensile test values are measured in the longitudinal direction in accordance with A 370 Test Methods and Definitions
- Mechanical test is not carried out. Mechanical test is carried out only when specified at the time of enquiry and order.
Soğuk Haddeleme Sonrası Yığın Tavlama Prosesinden Geçirilmek Şartıyla Soğuk Mamul Üretimine Uygun Sıcak Haddelenmiş Düşük Mukavemetli Çelikler
- Mechanical test is not carried out.
- The limitation requests for the residual elements (Cu, Ni, Cr, Mo) which are not mentioned on the table are subjected to negotitation for special application purposes.
- Suitable for batch annealing after cold reducing.
- Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.
- Tensile test values are measured in the longitudinal direction in accordance with A 370 Test Methods and Definitions
- Mechanical test is not carried out. Mechanical test is carried out only when specified at the time of enquiry and order.