6345 جودةمواصفات الورقة

6345 جودة مواصفات الورقة

Hot rolled steels for pressure purposes (boilers, steam boiler plants, pressure vessels, etc.) at elevated temperatures

البدائللا يوجد بديل لهذه الورقة.

Flat / Hot Rolled

Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.

Hot rolled steels for pressure purposes (boilers, steam boiler plants, pressure vessels, etc.) at elevated temperatures

التركيب الكيميائي (%)

المعيار المكافئرقم جودة إرديميرCmin.Cmax.Mnmin.Mnmax.Pmax.Smax.Simax.Nmax.Crmax.Momin.Momax.Nimax.Cumax.
المعيارجودة
EN 10028-2:201716Mo363450.120.200.400.900.0250.010.35120.000.300.250.350.300.30
  1. Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.

الخواص الميكانيكية

المعيار المكافئرقم جودة إرديميرRe [N/mm2] t(thickness, mm)Rm [N/mm2]A(%) min. t(thickness, mm)Impact
المعيارجودة
1.8≤t≤1616.01≤t≤26A801.8≤t≤2.99A53≤t≤26Temperature ( ° C)6≤t≤7.49KVC J min.6≤t≤7.49Temperature ( ° C)7.5≤t≤9.99KVC J min.7.5≤t≤9.99Temperature ( ° C)10≤t≤26KVC J min.10≤t≤26
EN 10028-2:201716Mo36345275 min.270 min.440-5902222201420212027
  1. Tensile test values apply to "transverse" test pieces
  2. The tensile test for proof strength at elevated temperature is carried out on request.
  3. Impact test is not carried out for thickness thinner than 6 mm.
  4. Depending on agreement the impact energy can be specified as 40J in the purchase order.

Flat / Plate

Heavy plate products are obtained by rolling semi-finished products with a rectangular cross-section (slab) produced by the continuous casting method to a specific temperature, with thicknesses ranging from 6.00 to 200.00 mm and widths ranging from 1000 to 3600 mm.

Hot rolled steels for pressure purposes (boilers, steam boiler plants, pressure vessels, etc.) at elevated temperatures

التركيب الكيميائي (%)

المعيار المكافئرقم جودة إرديميرCmin.Cmax.Mnmin.Mnmax.Pmax.Smax.Simax.Nmax.Crmax.Momin.Momax.Nimax.Cumax.
المعيارجودة
EN 10028-2:201716Mo363450.120.200.400.900.0250.010.35120.000.300.250.350.300.30
  1. Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.

الخواص الميكانيكية

المعيار المكافئرقم جودة إرديميرRe [N/mm2] t(thickness, mm)Rm [N/mm2]A(%) min.Impact
المعيارجودة
6≤t≤1616.01≤t≤4040.01≤t≤50A5Temperature ( ° C)6≤t≤7.49KVC J min.6≤t≤7.49Temperature ( ° C)7.5≤t≤9.99KVC J min.7.5≤t≤9.99Temperature ( ° C)10≤t≤60KVC J min.10≤t≤60
EN 10028-2:201716Mo36345275 min.270 min.260 min.440-59022201420212027
  1. Tensile test values apply to "transverse" test pieces
  2. The tensile test for proof strength at elevated temperature is carried out on request.
  3. Impact test is not carried out for thickness thinner than 6 mm.
  4. Depending on agreement the impact energy can be specified as 40J in the purchase order.