735 جودةمواصفات الورقة

735 جودة مواصفات الورقة

High-strength structural steels for manufacture of any kind of machines and machine parts, general construction, road and railway vehicles

البدائللا يوجد بديل لهذه الورقة.

Flat / Hot Rolled

Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.

High-strength structural steels for manufacture of any kind of machines and machine parts, general construction, road and railway vehicles

التركيب الكيميائي (%)

المعيار المكافئرقم جودة إرديميرCmin.Cmax.Mnmax.Pmax.Smax.Simax.Almin.Almax.Vmax.
المعيارجودة
SAE J403-20141022 (MOD)7350.170.221.600.030.0350.550.020.050.01
  1. Grade specified on the table, is produced within the framework of agreements with customers.
  2. The limitation requests for the residual elements (Cu, Ni, Cr, Mo) which are not mentioned on the table are subjected to negotitation for special application purposes.

الخواص الميكانيكية

المعيار المكافئرقم جودة إرديميرRe [N/mm2]Rm [N/mm2]A(%) min. t(thickness, mm)ImpactBend (Transverse , BMD) t: thickness
المعيارجودة
A801.8≤t≤2.99A53≤t≤18A518.01≤t≤20Temperature ( ° C)6≤t≤7.49KVC J min.6≤t≤7.49Temperature ( ° C)7.5≤t≤9.99KVC J min.7.5≤t≤9.99Temperature ( ° C)10≤t≤16KVC J min.10≤t≤16180°
SAE J403-20141022 (MOD)735345 min.517 min.202020-2014-2021-2027R 2d
  1. Tensile test values apply to "transverse" test pieces
  2. The impact test is carried out only when specified at the time of enquiry and order and is not carried out for thickness thinner than 6 mm.
  3. The bending test is carried out only when specified at the time of enquiry and order.

High-strength structural steels for manufacture of any kind of machines and machine parts, general construction, road and railway vehicles

التركيب الكيميائي (%)

المعيار المكافئرقم جودة إرديميرCmin.Cmax.Mnmax.Pmax.Smax.Simax.Almin.Almax.Vmax.
المعيارجودة
B105-20101022 (MOD)7350.170.221.600.030.0350.550.020.050.01
  1. Grade specified on the table, is produced within the framework of agreements with customers.
  2. The limitation requests for the residual elements (Cu, Ni, Cr, Mo) which are not mentioned on the table are subjected to negotitation for special application purposes.

الخواص الميكانيكية

المعيار المكافئرقم جودة إرديميرRe [N/mm2]Rm [N/mm2]A(%) min. t(thickness, mm)ImpactBend (Transverse , BMD) t: thickness
المعيارجودة
A801.8≤t≤2.99A53≤t≤18A518.01≤t≤20Temperature ( ° C)6≤t≤7.49KVC J min.6≤t≤7.49Temperature ( ° C)7.5≤t≤9.99KVC J min.7.5≤t≤9.99Temperature ( ° C)10≤t≤16KVC J min.10≤t≤16180°
B105-20101022 (MOD)735345 min.517 min.202020-2014-2021-2027R 2d
  1. Tensile test values apply to "transverse" test pieces
  2. The impact test is carried out only when specified at the time of enquiry and order and is not carried out for thickness thinner than 6 mm.
  3. The bending test is carried out only when specified at the time of enquiry and order.