1304 Quality Sheet Specification
Zinc coated (galvanized) low carbon steels for cold forming
AlternativesThere is no alternative to this sheet.
Flat / Galvanised
Galvanized flat steel is manufactured by zinc-coating both sides of cold rolled metal by hot-dipping process. After having coated the steel surface with zinc, the coating of the interface is transformed into an alloy of iron-zinc layer through heating by induction and the galvannealed steel is produced.
Zinc coated (galvanized) low carbon steels for cold forming
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmax. | Mnmax. | Pmax. | Smax. | Simax. | Timax. | |
|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||
| EN 10346:2015 | DX54D+Z | 1304 | 0.12 | 0.60 | 0.10 | 0.045 | 0.50 | 0.30 |
- There are no chemical footnotes.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | n90 | r90 | |||||
|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||||||
| A800.4≤t≤0.5 | A800.51≤t≤0.7 | A800.71≤t≤2 | min. | 0.4≤t≤1.5 | 1.51≤t≤1.99 | 2≤t≤2.1 | |||||
| EN 10346:2015 | DX54D+Z | 1304 | 120-220 | 260-350 | 32 | 34 | 36 | 0.18 | 1.6 min. | 1.4 min. | 1.2 min. |
- Tensile test values apply to "transverse" test pieces
- For surface quality A, the upper value for yield strength is 360MPa.
- Guarantee periods of absence of stretcher strains marks and mechanical properties are 6 months. The period begin on the date on which products are made available.