1630 Quality Sheet Specification
High strength, low alloyed, zinc coated (galvanized) steels by continous hot-dip process for cold forming
AlternativesThere is no alternative to this sheet.
Flat / Galvanised
Galvanized flat steel is manufactured by zinc-coating both sides of cold rolled metal by hot-dipping process. After having coated the steel surface with zinc, the coating of the interface is transformed into an alloy of iron-zinc layer through heating by induction and the galvannealed steel is produced.
High strength, low alloyed, zinc coated (galvanized) steels by continous hot-dip process for cold forming
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmax. | Mnmax. | Pmax. | Smax. | Simax. | Almin. | Nbmax. | Timax. | |
|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||||
| EN 10346:2015 | HX300LAD+Z | 1630 | 0.12 | 1.40 | 0.03 | 0.025 | 0.50 | 0.015 | 0.09 | 0.15 |
- There are no chemical footnotes.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | |||
|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||
| A800.4≤t≤0.5 | A800.51≤t≤0.7 | A800.71≤t≤2 | |||||
| EN 10346:2015 | HX300LAD+Z | 1630 | 300-380 | 380-480 | 19 | 21 | 23 |
- Tensile test values apply to "transverse" test pieces
- The mechanical properties are valid for a period of 6 months from the date on which the products are made available.