6860 Quality Sheet Specification
Orta ve Düşük Sıcaklıklarda Ve Basınç Altında Kullanıma Uygun Karbon Çelikleri
AlternativesThere is no alternative to this sheet.
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Orta ve Düşük Sıcaklıklarda Ve Basınç Altında Kullanıma Uygun Karbon Çelikleri
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Thickness (mm) | Cmax. | Mnmin. | Mnmax. | Pmax. | Smax. | Simin. | Simax. | Crmax. | Momax. | Nimax. | Vmax. | Nbmax. | Timax. | Cumax. | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||||||||||||
| ASTM A516-2025 | 60 | 6860 | 1≤t≤12.5 | 0.21 | 0.60 | 0.90 | 0.025 | 0.025 | 0.15 | 0.40 | 0.30 | 0.12 | 0.40 | 0.03 | 0.02 | 0.03 | 0.40 |
| ASTM A516-2025 | 60 | 6860 | 12.51≤t≤20 | 0.23 | 0.85 | 1.20 | 0.025 | 0.025 | 0.15 | 0.40 | 0.30 | 0.12 | 0.40 | 0.03 | 0.02 | 0.03 | 0.40 |
- Grade 6860 products 12.5mm and under in thickness may have 0.85-1.20 % manganese on heat analysis and 0.79-1.30 % manganese on product analysis.
- For each reduction of 0.01 percentage point below the specified maximum for carbon, an increase of 0.06 percentage point above the specified maximum for manganese is permitted up to a maximum of 1.50% by heat analysis and 1.60% by product analysis.
- Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | Impact | |||||
|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||||
| A501.8≤t≤19 | A20019.01≤t≤26 | Temperature ( ° C)10≤t≤25 | KVC J min.10≤t≤25 | Temperature ( ° C)25.01≤t≤26 | KVC J min.25.01≤t≤26 | |||||
| ASTM A516-2025 | 60 | 6860 | 220 min. | 415-550 | 25 | 21 | -51 | 18 | -46 | 18 |
- When notch-toughness tests are required, the plates shall be normalized unless otherwise specified by the purchaser.
- Tensile test values apply to "transverse" test pieces
- Impact energy values for "full size" (10 X 10 mm) test specimens for thinner products, impact energy values decreases depending on the thickness.
- The impact test is carried out only when specified at the time of enquiry and order and is not carried out for thickness thinner than 6 mm.
Flat / Plate
Heavy plate products are obtained by rolling semi-finished products with a rectangular cross-section (slab) produced by the continuous casting method to a specific temperature, with thicknesses ranging from 6.00 to 200.00 mm and widths ranging from 1000 to 3600 mm.
Orta ve Düşük Sıcaklıklarda Ve Basınç Altında Kullanıma Uygun Karbon Çelikleri
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Thickness (mm) | Cmax. | Mnmin. | Mnmax. | Pmax. | Smax. | Simin. | Simax. | Crmax. | Momax. | Nimax. | Vmax. | Nbmax. | Timax. | Cumax. | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||||||||||||
| ASTM A516-2025 | 60 | 6860 | 6≤t≤12.5 | 0.21 | 0.60 | 0.90 | 0.025 | 0.025 | 0.15 | 0.40 | 0.30 | 0.12 | 0.40 | 0.03 | 0.02 | 0.03 | 0.40 |
| ASTM A516-2025 | 60 | 6860 | 12.51≤t≤50 | 0.23 | 0.85 | 1.20 | 0.025 | 0.025 | 0.15 | 0.40 | 0.30 | 0.12 | 0.40 | 0.03 | 0.02 | 0.03 | 0.40 |
| ASTM A516-2025 | 60 | 6860 | 50.01≤t≤60 | 0.25 | 0.85 | 1.20 | 0.025 | 0.025 | 0.15 | 0.40 | 0.30 | 0.12 | 0.40 | 0.03 | 0.02 | 0.03 | 0.40 |
- Grade 6860 products 12.5mm and under in thickness may have 0.85-1.20 % manganese on heat analysis and 0.79-1.30 % manganese on product analysis.
- For each reduction of 0.01 percentage point below the specified maximum for carbon, an increase of 0.06 percentage point above the specified maximum for manganese is permitted up to a maximum of 1.50% by heat analysis and 1.60% by product analysis.
- Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | Impact | |||||
|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||||
| A506≤t≤19 | A20019.01≤t≤60 | Temperature ( ° C)10≤t≤25 | KVC J min.10≤t≤25 | Temperature ( ° C)25.01≤t≤60 | KVC J min.25.01≤t≤60 | |||||
| ASTM A516-2025 | 60 | 6860 | 220 min. | 415-550 | 25 | 21 | -51 | 18 | -46 | 18 |
- Tensile test values apply to "transverse" test pieces
- Impact energy values for "full size" (10 X 10 mm) test specimens for thinner products, impact energy values decreases depending on the thickness.
- The impact test is carried out only when specified at the time of enquiry and order and is not carried out for thickness thinner than 6 mm.
- Plate thickness > 40 mm shall be normalized. When notch-toughness tests are required on plates 40 mm and under in thickness, the plates shall be normalized unless otherwise specified by the purchaser.