6345 Quality Sheet Specification
Hot rolled steels for pressure purposes (boilers, steam boiler plants, pressure vessels, etc.) at elevated temperatures
AlternativesThere is no alternative to this sheet.
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Hot rolled steels for pressure purposes (boilers, steam boiler plants, pressure vessels, etc.) at elevated temperatures
- Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.
- Tensile test values apply to "transverse" test pieces
- The tensile test for proof strength at elevated temperature is carried out on request.
- Impact test is not carried out for thickness thinner than 6 mm.
- Depending on agreement the impact energy can be specified as 40J in the purchase order.
Flat / Plate
Heavy plate products are obtained by rolling semi-finished products with a rectangular cross-section (slab) produced by the continuous casting method to a specific temperature, with thicknesses ranging from 6.00 to 200.00 mm and widths ranging from 1000 to 3600 mm.
Hot rolled steels for pressure purposes (boilers, steam boiler plants, pressure vessels, etc.) at elevated temperatures
- Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.
- Tensile test values apply to "transverse" test pieces
- The tensile test for proof strength at elevated temperature is carried out on request.
- Impact test is not carried out for thickness thinner than 6 mm.
- Depending on agreement the impact energy can be specified as 40J in the purchase order.