3436 Quality Sheet Specification
Katlamaya Uygun Yapı Çelikleri
AlternativesThere is no alternative to this sheet.
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Katlamaya Uygun Yapı Çelikleri
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmax. | Mnmax. | Pmax. | Smax. | Crmax. | Momax. | Nimax. | Vmax. | Nbmax. | Timax. | Cumax. | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||||||||
| ASTM A1018-2025 | SS 36 Type 1 | 3436 | 0.25 | 1.50 | 0.035 | 0.04 | 0.15 | 0.06 | 0.20 | 0.008 | 0.008 | 0.025 | 0.20 |
- Titanium is permitted at the producer’s option, to the lesser of 3.4N + 1.5S or 0.025 %.
- When copper is requested in the chemical compositon, value specified in the table will be evaluated as minimum value. When copper is not specified, the copper limit is a maximum requirement.
- For thickness ≥ 20 mm, the manganese content is from 0.80 to 1.20 % max. For each reduction of 0.01% below the specified carbon maximum, an increase of 0.06% manganese above the specified maximum will be permitted up to a maximum of 1.35%.
- Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | |
|---|---|---|---|---|
| Standard | Quality | |||
| ASTM A1018-2025 | SS 36 Type 1 | 3436 | 250 min. | 365 min. |
- Tensile test values apply to "transverse" test pieces
- The bending test and impact test are carried out only when specified at the time of enquiry and order.