392 Quality Sheet Specification
Galvanized,dual-phase steel with high yield strength for cold forming
AlternativesThere is no alternative to this sheet.
Flat / Galvanised
Galvanized flat steel is manufactured by zinc-coating both sides of cold rolled metal by hot-dipping process. After having coated the steel surface with zinc, the coating of the interface is transformed into an alloy of iron-zinc layer through heating by induction and the galvannealed steel is produced.
Galvanized,dual-phase steel with high yield strength for cold forming
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmax. | Mnmax. | Pmax. | Smax. | Simax. | Almin. | Cumax. | Bmax. | |
|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||||
| 52815/9.52873 | FE 600 DP F-ZNT/F/2S | 392 | 0.23 | 3.30 | 0.09 | 0.015 | 2.00 | 0.01 | 0.20 | 60.00 |
- If the carbon value %C < 0.015 , contains a minimum of 0.0003% (3 ppm) boron.
- %Ni+%Cr+%Mo ≤ 1.5
- The limits which are specified in the table are the limits of the customer's specifications.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | BH2 [N/mm2] min. | |||
|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||
| A800.4≤t≤0.49 | A800.5≤t≤0.7 | A800.71≤t≤2 | ||||||
| 52815/9.52873 | FE 600 DP F-ZNT/F/2S | 392 | 340-400 | 590 min. | 16 | 18 | 20 | 30 |
- If the maximumu value of uniform elongation is lower than 20 %, the value of n is determined between 10 % and Ag % (the maximum value of uniform elongation)
- The mechanical properties are valid for a period of 3 months from the date on which the products are made available.
- Tensile test values apply to "longitudinal" test pieces