376 Quality Sheet Specification
High strength, low alloyed, zinc coated (galvanized) steels by continous hot-dip process for cold forming
AlternativesThere is no alternative to this sheet.
Flat / Galvanised
Galvanized flat steel is manufactured by zinc-coating both sides of cold rolled metal by hot-dipping process. After having coated the steel surface with zinc, the coating of the interface is transformed into an alloy of iron-zinc layer through heating by induction and the galvannealed steel is produced.
High strength, low alloyed, zinc coated (galvanized) steels by continous hot-dip process for cold forming
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmax. | Mnmax. | Pmax. | Smax. | Simax. | Almin. | Nbmax. | Timax. | |
|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||||
| WSS-M1A367 | A36 | 376 | 0.12 | 1.50 | 0.03 | 0.025 | 0.50 | 0.015 | 0.09 | 0.15 |
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | A(%) min. | n90 | |
|---|---|---|---|---|---|---|
| Standard | Quality | |||||
| A80 | min. | |||||
| WSS-M1A367 | A36 | 376 | 340-420 | 410-530 | 20 | 0.13 |
- The mechanical properties are valid for a period of 6 months from the date on which the products are made available.
- Unless otherwise agreed, n value is taken between %10-20 elongation range.
- Tensile test values apply to "longitudinal" test pieces