432 Quality Sheet Specification
Zinc-iron alloy coated (galvannealed) low carbon steels for cold forming
AlternativesThere is no alternative to this sheet.
Flat / Galvanised
Galvanized flat steel is manufactured by zinc-coating both sides of cold rolled metal by hot-dipping process. After having coated the steel surface with zinc, the coating of the interface is transformed into an alloy of iron-zinc layer through heating by induction and the galvannealed steel is produced.
Zinc-iron alloy coated (galvannealed) low carbon steels for cold forming
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmax. | Mnmax. | Pmax. | Smax. | Nbmax. | Timax. | |
|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||
| HES C071 | JAC270F | 432 | 0.008 | 0.25 | 0.025 | 0.02 | 0.04 | 0.10 |
- Chemical composition is not specified in customer specification. Limits given in this table are based on Erdemir practice for reference.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | rort | ||
|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||
| A80 | A50 | ||||||
| HES C071 | JAC270F | 432 | 110-175 | 270 min. | 38-47 | 46-56 | 1.5 min. |
- The mechanical properties are valid for a period of 12 months from the date on which the products are made available.
- Tensile test values apply to "longitudinal" test pieces