5152 QualitySheet Specification

5152 Quality Sheet Specification

Hot rolled unalloyed structural steels for manufacture of construction equipment, machines and various machine parts, general construction plates, road and railway vehicles

AlternativesThere is no alternative to this sheet.

Flat / Plate

Heavy plate products are obtained by rolling semi-finished products with a rectangular cross-section (slab) produced by the continuous casting method to a specific temperature, with thicknesses ranging from 6.00 to 200.00 mm and widths ranging from 1000 to 3600 mm.

Hot rolled unalloyed structural steels for manufacture of construction equipment, machines and various machine parts, general construction plates, road and railway vehicles

Chemical Composition (%)

Standard EquivalentErdemir Grade NoThickness (mm)Cmax.Mnmax.Pmax.Smax.Simax.Nmax.Cumax.CEmax.
StandardQuality
EN 10025-2:2019S355J0+AR Mod51526≤t≤300.201.600.030.030.55120.000.550.45
EN 10025-2:2019S355J0+AR Mod515230.01≤t≤1000.221.600.030.030.55120.000.550.45
  1. This grade is produced as "Mod" with a carbon equivalent limit. Carbon equivalent, CEV (IIW) % = C + Mn / 6 + (Cr + Mo + V) / 5 + (Ni + Cu) / 15
  2. The maximum value for nitrogen does not apply if the chemical composition shows a minimum total aluminium content of 0.020%.
  3. Produced as Plate Product
  4. C = 0.22 % max. for thickness greater than 30 mm,

Mechanical Properties

Standard EquivalentErdemir Grade NoRe [N/mm2] t(thickness, mm)Rm [N/mm2]A(%) min. t(thickness, mm)Impact
StandardQuality
6≤t≤1616.01≤t≤4040.01≤t≤6363.01≤t≤8080.01≤t≤100A58≤t≤40A540.01≤t≤63A563.01≤t≤100Temperature ( ° C)6≤t≤7.49KVC J min.6≤t≤7.49Temperature ( ° C)7.5≤t≤9.99KVC J min.7.5≤t≤9.99Temperature ( ° C)10≤t≤100KVC J min.10≤t≤100
EN 10025-2:2019S355J0+AR Mod5152355 min.345 min.335 min.325 min.315 min.470-630201918014021027
  1. Tensile test values apply to "transverse" test pieces