6006 Quality Sheet Specification
Low and medium strength carbon steels (automotive industry, pipe and machine parts production)
Reproducible Letter Symbols --> DS --> HRP --> HRPKK --> HRU --> HRUKK --> KRKK --> L --> LKK --> LP --> LPKK --> LR --> LRKK --> R --> RD --> RKK --> RP --> RPD --> RPKK --> THRU --> TR --> TRKK --> TRP
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Low and medium strength carbon steels (automotive industry, pipe and machine parts production)
- The limitation requests for the residual elements (Cu, Ni, Cr, Mo) which are not mentioned on the table are subjected to negotitation for special application purposes.
- When Silicon ranges or limits are required, the following ranges are commonly used 0,10 % max; 0,10 to 0,20 %; 0,15 to 0,35 %; 0,20 to 0,40 %; or 0,30 to 0,60 %. Erdemir normally applies the above silicon ranges but they can be also produced in the other silicon ranges.
- Tensile test values are measured in the longitudinal direction in accordance with A 370 Test Methods and Definitions
- Mechanical test is not carried out. Mechanical test is carried out only when specified at the time of enquiry and order.
Düşük ve Orta Mukavemetli Karbon Çelikleri (Otomotiv Sanayi, Boru, Profil ve Muhtelif Makine)
- The limitation requests for the residual elements (Cu, Ni, Cr, Mo) which are not mentioned on the table are subjected to negotitation for special application purposes.
- When Silicon ranges or limits are required, the following ranges are commonly used 0,10 % max; 0,10 to 0,20 %; 0,15 to 0,35 %; 0,20 to 0,40 %; or 0,30 to 0,60 %. Erdemir normally applies the above silicon ranges but they can be also produced in the other silicon ranges.
- Tensile test values are measured in the longitudinal direction in accordance with A 370 Test Methods and Definitions
- Mechanical test is not carried out. Mechanical test is carried out only when specified at the time of enquiry and order.
Düşük ve Orta Mukavemetli Karbon Çelikleri (Otomotiv Sanayi, Boru, Profil ve Muhtelif Makine Parçası İmalatı)
- The limitation requests for the residual elements (Cu, Ni, Cr, Mo) which are not mentioned on the table are subjected to negotitation for special application purposes.
- When Silicon ranges or limits are required, the following ranges are commonly used 0,10 % max; 0,10 to 0,20 %; 0,15 to 0,35 %; 0,20 to 0,40 %; or 0,30 to 0,60 %. Erdemir normally applies the above silicon ranges but they can be also produced in the other silicon ranges.
- Tensile test values are measured in the longitudinal direction in accordance with A 370 Test Methods and Definitions
- Mechanical test is not carried out. Mechanical test is carried out only when specified at the time of enquiry and order.
Flat / Plate
Heavy plate products are obtained by rolling semi-finished products with a rectangular cross-section (slab) produced by the continuous casting method to a specific temperature, with thicknesses ranging from 6.00 to 200.00 mm and widths ranging from 1000 to 3600 mm.
Low and medium strength carbon steels (automotive industry, pipe and machine parts production)
- The limitation requests for the residual elements (Cu, Ni, Cr, Mo) which are not mentioned on the table are subjected to negotitation for special application purposes.
- For plate products, they are produced only according to SAE standards.
- When Silicon ranges or limits are required, the following ranges are commonly used 0,10 % max; 0,10 to 0,20 %; 0,15 to 0,35 %; 0,20 to 0,40 %; or 0,30 to 0,60 %. Erdemir normally applies the above silicon ranges but they can be also produced in the other silicon ranges.
- Tensile test values are measured in the longitudinal direction in accordance with A 370 Test Methods and Definitions
- Mechanical test is not carried out. Mechanical test is carried out only when specified at the time of enquiry and order.
Düşük ve Orta Mukavemetli Karbon Çelikleri (Otomotiv Sanayi, Boru, Profil ve Muhtelif Makine)
- The limitation requests for the residual elements (Cu, Ni, Cr, Mo) which are not mentioned on the table are subjected to negotitation for special application purposes.
- For plate products, they are produced only according to SAE standards.
- When Silicon ranges or limits are required, the following ranges are commonly used 0,10 % max; 0,10 to 0,20 %; 0,15 to 0,35 %; 0,20 to 0,40 %; or 0,30 to 0,60 %. Erdemir normally applies the above silicon ranges but they can be also produced in the other silicon ranges.
- Tensile test values are measured in the longitudinal direction in accordance with A 370 Test Methods and Definitions
- Mechanical test is not carried out. Mechanical test is carried out only when specified at the time of enquiry and order.
Düşük ve Orta Mukavemetli Karbon Çelikleri (Otomotiv Sanayi, Boru, Profil ve Muhtelif Makine Parçası İmalatı)
- The limitation requests for the residual elements (Cu, Ni, Cr, Mo) which are not mentioned on the table are subjected to negotitation for special application purposes.
- For plate products, they are produced only according to SAE standards.
- When Silicon ranges or limits are required, the following ranges are commonly used 0,10 % max; 0,10 to 0,20 %; 0,15 to 0,35 %; 0,20 to 0,40 %; or 0,30 to 0,60 %. Erdemir normally applies the above silicon ranges but they can be also produced in the other silicon ranges.
- Tensile test values are measured in the longitudinal direction in accordance with A 370 Test Methods and Definitions
- Mechanical test is not carried out. Mechanical test is carried out only when specified at the time of enquiry and order.