841 Quality Sheet Specification
Hot rolled high yield strength steels suitable for cold forming
AlternativesThere is no alternative to this sheet.
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Hot rolled high yield strength steels suitable for cold forming
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmax. | Mnmax. | Pmax. | Smax. | Simax. | Almin. | Nbmax. | Timax. | Cumax. | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||||||
| RNES-B-20070_2.0 | HR420LA | 841 | 0.12 | 1.60 | 0.03 | 0.025 | 0.50 | 0.015 | 0.10 | 0.15 | 0.20 |
- Grade specified on the table, is produced within the framework of agreements with customers.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | ||
|---|---|---|---|---|---|---|
| Standard | Quality | |||||
| A802≤t≤2.99 | A53≤t≤8 | |||||
| RNES-B-20070_2.0 | HR420LA | 841 | 420-520 | 480-600 | 18 | 22 |
- Tensile test values apply to "longitudinal" test pieces
- The mechanical properties are valid for a period of 6 months from the date on which the products are made available.