9329 Quality Sheet Specification
Hot rolled weldable fine-grained structural steels
AlternativesThere is no alternative to this sheet.
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Hot rolled weldable fine-grained structural steels
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Thickness (mm) | Cmax. | Mnmin. | Mnmax. | Pmax. | Smax. | Simax. | Vmin. | Vmax. | Cumin. | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||||||
| ASTM A572-2018 | 42 Type2 | 9329 | 1≤t≤10 | 0.21 | 0.50 | 1.35 | 0.03 | 0.03 | 0.40 | 0.01 | 0.15 | 0.20 |
| ASTM A572-2018 | 42 Type2 | 9329 | 10.01≤t≤25 | 0.21 | 0.80 | 1.35 | 0.03 | 0.03 | 0.40 | 0.01 | 0.15 | 0.20 |
- Copper content shall be min 0.20% when Cu steel is specified.
- For each reduction of 0.01 percentage point below the specified carbon maximum, an increase of 0.06 percentage point manganese above the specified maximum is permitted, up to a maximum of 1.60 %.
- Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.
- The manganese to carbon ratio shall not be less than 2 to 1.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | ||
|---|---|---|---|---|---|---|
| Standard | Quality | |||||
| A502≤t≤19 | A20019.01≤t≤26 | |||||
| ASTM A572-2018 | 42 Type2 | 9329 | 290 min. | 415 min. | 22 | 18 |
- Tensile test values apply to "transverse" test pieces
Flat / Plate
Heavy plate products are obtained by rolling semi-finished products with a rectangular cross-section (slab) produced by the continuous casting method to a specific temperature, with thicknesses ranging from 6.00 to 200.00 mm and widths ranging from 1000 to 3600 mm.
Hot rolled weldable fine-grained structural steels
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Thickness (mm) | Cmax. | Mnmin. | Mnmax. | Pmax. | Smax. | Simax. | Vmin. | Vmax. | Cumin. | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||||||
| ASTM A572-2018 | 42 Type2 | 9329 | 6≤t≤10 | 0.21 | 0.50 | 1.35 | 0.03 | 0.03 | 0.40 | 0.01 | 0.15 | 0.20 |
| ASTM A572-2018 | 42 Type2 | 9329 | 10.01≤t≤40 | 0.21 | 0.80 | 1.35 | 0.03 | 0.03 | 0.40 | 0.01 | 0.15 | 0.20 |
- Copper content shall be min 0.20% when Cu steel is specified.
- For each reduction of 0.01 percentage point below the specified carbon maximum, an increase of 0.06 percentage point manganese above the specified maximum is permitted, up to a maximum of 1.60 %.
- Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.
- Silicon content is ≥ 0.15% for thickness greater than 40 mm.
- The manganese to carbon ratio shall not be less than 2 to 1.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | ||
|---|---|---|---|---|---|---|
| Standard | Quality | |||||
| A506≤t≤19 | A20019.01≤t≤60 | |||||
| ASTM A572-2018 | 42 Type2 | 9329 | 290 min. | 415 min. | 22 | 18 |
- Tensile test values apply to "transverse" test pieces