9355 Quality Sheet Specification
Hot rolled weldable fine-grained normalized structural steels
Reproducible Letter Symbols --> HRP --> HRPKK --> HRU --> HRUKK --> KRKK --> LP --> LPKK --> LR --> LRKK --> RD --> RKK --> RP --> RPD --> RPKK
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Hot rolled weldable fine-grained normalized structural steels
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmax. | Mnmin. | Mnmax. | Pmax. | Smax. | Simax. | Almin. | Nmax. | Crmax. | Momax. | Nimax. | Vmax. | Nbmax. | Timax. | Cumax. | CEmax. | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||||||||||||
| EN 10025-3:2019 | S355N | 9355 | 0.20 | 0.90 | 1.65 | 0.03 | 0.025 | 0.50 | 0.02 | 150.00 | 0.30 | 0.10 | 0.50 | 0.12 | 0.05 | 0.05 | 0.55 | 0.43 |
- Max carbon equivalent (CE) is increased by 0.01 % for Si ≤ 0.25%, and 0.02 % for Si ≤ 0.030 %
- If sufficient nitrogen-binding elements are present, the minimum total aluminium content does not apply.
- Carbon equivalent, CEV (IIW) % = C + Mn / 6 + (Cr + Mo + V) / 5 + (Ni + Cu) / 15
- This grade is produced normalized or equivalent to normalized rolling.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] t(thickness, mm) | Rm [N/mm2] | A(%) min. | Impact | Bend (Transverse , BMD) t: thickness | |||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||||||||
| 2.1≤t≤16 | 16.01≤t≤26 | A5 | Temperature ( ° C)6≤t≤7.49 | KVC J min.6≤t≤7.49 | Temperature ( ° C)7.5≤t≤9.99 | KVC J min.7.5≤t≤9.99 | Temperature ( ° C)10≤t≤26 | KVC J min.10≤t≤26 | 180° | ||||
| EN 10025-3:2019 | S355N | 9355 | 355 min. | 345 min. | 470-630 | 22 | -20 | 20 | -20 | 30 | -20 | 40 | R 2d |
- Tensile test values apply to "transverse" test pieces
- Impact test is not carried out for thickness thinner than 6 mm.
- Bending test is not carried out for thickness greater than 12 mm.
- The bending test is carried out only when specified at the time of enquiry and order.
Flat / Plate
Heavy plate products are obtained by rolling semi-finished products with a rectangular cross-section (slab) produced by the continuous casting method to a specific temperature, with thicknesses ranging from 6.00 to 200.00 mm and widths ranging from 1000 to 3600 mm.
Hot rolled weldable fine-grained normalized structural steels
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmax. | Mnmin. | Mnmax. | Pmax. | Smax. | Simax. | Almin. | Nmax. | Crmax. | Momax. | Nimax. | Vmax. | Nbmax. | Timax. | Cumax. | CEmax. | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||||||||||||
| EN 10025-3:2019 | S355N | 9355 | 0.20 | 0.90 | 1.65 | 0.03 | 0.025 | 0.50 | 0.02 | 150.00 | 0.30 | 0.10 | 0.50 | 0.12 | 0.05 | 0.05 | 0.55 | 0.43 |
- Max carbon equivalent (CE) is increased by 0.01 % for Si ≤ 0.25%, and 0.02 % for Si ≤ 0.030 %
- If sufficient nitrogen-binding elements are present, the minimum total aluminium content does not apply.
- Carbon equivalent, CEV (IIW) % = C + Mn / 6 + (Cr + Mo + V) / 5 + (Ni + Cu) / 15
- This grade is produced normalized or equivalent to normalized rolling.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] t(thickness, mm) | Rm [N/mm2] | A(%) min. | Impact | Bend (Transverse , BMD) t: thickness | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||||||||
| 6≤t≤16 | 16.01≤t≤40 | 40.01≤t≤60 | A5 | Temperature ( ° C)6≤t≤7.49 | KVC J min.6≤t≤7.49 | Temperature ( ° C)7.5≤t≤9.99 | KVC J min.7.5≤t≤9.99 | Temperature ( ° C)10≤t≤60 | KVC J min.10≤t≤60 | 180° | ||||
| EN 10025-3:2019 | S355N | 9355 | 355 min. | 345 min. | 335 min. | 470-630 | 22 | -20 | 20 | -20 | 30 | -20 | 40 | R 2d |
- Tensile test values apply to "transverse" test pieces
- Impact test is not carried out for thickness thinner than 6 mm.
- Bending test is not carried out for thickness greater than 16 mm.
- The bending test is carried out only when specified at the time of enquiry and order.