9500 QualitySheet Specification

9500 Quality Sheet Specification

Hot rolled high strength structural steel for casing

AlternativesThere is no alternative to this sheet.

Flat / Hot Rolled

Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.

Hot rolled high strength structural steel for casing

Chemical Composition (%)

Standard Equivalent		Erdemir Grade No	Cmax.	Mnmin.	Mnmax.	Pmax.	Smax.	Simax.	Almin.	Crmax.	Momax.	Nimax.	Nbmax.	Timax.	Cumax.
Standard	Quality	Erdemir Grade No	Cmax.	Mnmin.	Mnmax.	Pmax.	Smax.	Simax.	Almin.	Crmax.	Momax.	Nimax.	Nbmax.	Timax.	Cumax.
ERDEMİR-2005	9500	9500	0.16	1.50	2.00	0.02	0.01	0.50	0.02	0.20	0.25	0.30	0.10	0.05	0.20

There are no chemical footnotes.

Mechanical Properties

Standard Equivalent		Erdemir Grade No	Re [N/mm2]	Rm [N/mm2]	A(%) min.	Impact						Bend (Transverse , BMD) t: thickness
Standard	Quality				A(%) min.	Impact						Bend (Transverse , BMD) t: thickness
Standard	Quality				A5	Temperature ( ° C)6≤t≤7.49	KVC J min.6≤t≤7.49	Temperature ( ° C)7.5≤t≤9.99	KVC J min.7.5≤t≤9.99	Temperature ( ° C)10≤t≤20	KVC J min.10≤t≤20	180°
ERDEMİR-2005	9500	9500	500 min.	690 min.	18	-20	15	-20	20	-20	30	R 4d

Tensile test values apply to "transverse" test pieces
The bending test and impact test are carried out only when specified at the time of enquiry and order.
The bending test and impact test are carried out only when specified at the time of enquiry and order.
Tensile test values apply to "transverse" test pieces
The impact test is carried out only when specified at the time of enquiry and order and is not carried out for thickness thinner than 6 mm.
The bending test is carried out only when specified at the time of enquiry and order.