365 Quality Sheet Specification
High strength, low alloyed, zinc coated (galvanized) steels by continous hot-dip process for cold forming
AlternativesThere is no alternative to this sheet.
Flat / Galvanised
Galvanized flat steel is manufactured by zinc-coating both sides of cold rolled metal by hot-dipping process. After having coated the steel surface with zinc, the coating of the interface is transformed into an alloy of iron-zinc layer through heating by induction and the galvannealed steel is produced.
High strength, low alloyed, zinc coated (galvanized) steels by continous hot-dip process for cold forming
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmax. | Mnmax. | Pmax. | Smax. | Simax. | Almin. | Vmax. | Nbmin. | Nbmax. | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||||||
| 52811/9.52873 | FEE 300 F - ZNT/F/2S | 365 | 0.12 | 1.30 | 0.03 | 0.03 | 0.50 | 0.015 | 0.10 | 0.03 | 0.07 |
- (Nb + V + Ti) ≤ 0.22%
- The V and Nb limits are specified as reference value according to Erdemir manufacturing practice. Other limits are customer specification limits.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | A(%) min. | n90 | |
|---|---|---|---|---|---|---|
| Standard | Quality | |||||
| A80 | min. | |||||
| 52811/9.52873 | FEE 300 F - ZNT/F/2S | 365 | 300-380 | 370 min. | 22 | 0.14 |
- "n" is average value.
- The mechanical properties are valid for a period of 6 months from the date on which the products are made available.
- Tensile test values apply to "longitudinal" test pieces