372 QualitySheet Specification

372 Quality Sheet Specification

High strength, low alloyed, zinc coated (galvanized) steels by continous hot-dip process for cold forming

Reproducible Letter Symbols --> GZR --> GZRD --> GZR
Alternatives355 366 367 1322 1325 1328 1332 1335

Flat / Galvanised

Galvanized flat steel is manufactured by zinc-coating both sides of cold rolled metal by hot-dipping process. After having coated the steel surface with zinc, the coating of the interface is transformed into an alloy of iron-zinc layer through heating by induction and the galvannealed steel is produced.

High strength, low alloyed, zinc coated (galvanized) steels by continous hot-dip process for cold forming

Chemical Composition (%)

Standard EquivalentErdemir Grade NoCmax.Mnmax.Pmax.Smax.Simax.Almin.Almax.Vmax.Nbmax.Timax.CEmax.
StandardQuality
11-04-002XE-360D3720.111.400.030.0250.500.0150.080.100.100.100.31
  1. The carbon equivalent is defined by the Ceq formula = C+(Mn+Si)/6.
  2. The limits which are specified in the table are the limits of the customer's specifications.

Mechanical Properties

Standard EquivalentErdemir Grade NoRe [N/mm2]Rm [N/mm2]Re/RmA(%) min.n90r90
StandardQuality
A80min.
11-04-002XE-360D372360-440450-5300.85 max.210.130.5 min.
  1. The mechanical properties are valid for a period of 6 months from the date on which the products are made available.
  2. Unless otherwise agreed, n value is taken between %10-20 elongation range.
  3. Tensile test values apply to "longitudinal" test pieces