3932 Quality Sheet Specification
High, medium strength steels for automotive industry, mostly for discs
AlternativesThere is no alternative to this sheet.
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
High, medium strength steels for automotive industry, mostly for discs
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Thickness (mm) | Cmin. | Cmax. | Mnmin. | Mnmax. | Pmax. | Smax. | Simax. | Almin. | Almax. | Nmax. | Cumax. | CEmax. | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||||||||||
| EN 10025-2:2019 | S235JR (MOD) | 3932 | 1.5≤t≤8 | 0.03 | 0.09 | 0.20 | 0.85 | 0.025 | 0.015 | 0.15 | 0.015 | 0.07 | 120.00 | 0.55 | 0.35 |
| EN 10025-2:2019 | S235JR (MOD) | 3932 | 8.01≤t≤25 | 0.09 | 0.17 | 0.20 | 0.85 | 0.025 | 0.015 | 0.15 | 0.015 | 0.07 | 120.00 | 0.55 | 0.35 |
- The maximum value for nitrogen does not apply if the chemical composition shows a minimum total aluminium content of 0.020%. Minimum aluminium to nitrogen ratio is 2:1.
- Carbon equivalent, CEV (IIW) % = C + Mn / 6 + (Cr + Mo + V) / 5 + (Ni + Cu) / 15
- If Cu %: 0.25-0.40, max carbon equivalent (CEV) is increased 0.02 % within the framework of agreements with customers.
- Could be normalized or equivalent to normalized rolling.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | Impact | ||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||||||||||
| A801.5≤t≤1.5 | A801.51≤t≤2 | A802.01≤t≤2.5 | A802.51≤t≤2.99 | A53≤t≤10 | Temperature ( ° C)6≤t≤7.49 | KVC J min.6≤t≤7.49 | Temperature ( ° C)7.5≤t≤9.99 | KVC J min.7.5≤t≤9.99 | Temperature ( ° C)10≤t≤25 | KVC J min.10≤t≤25 | |||||
| EN 10025-2:2019 | S235JR (MOD) | 3932 | 235 min. | 360-510 | 16 | 17 | 18 | 19 | 24 | 20 | 14 | 20 | 21 | 20 | 27 |
- Tensile test values apply to "transverse" test pieces
- The impact test is carried out only when specified at the time of enquiry and order and is not carried out for thickness thinner than 6 mm.
- This grade is produced according to reference mechanical values above in line with agreements with customers.