3960 Quality Sheet Specification
Hot Rolled Steels For Wheel Manufacturing Based On Customer Specification
Reproducible Letter Symbols --> HRUKK --> KRKK --> LRKK --> RKK
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Hot Rolled Steels For Wheel Manufacturing Based On Customer Specification
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmax. | Mnmax. | Pmax. | Smax. | Simax. | Almin. | Almax. | Nmax. | Vmax. | Nbmax. | Timax. | Cumax. | Snmax. | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||||||||||
| MW GL-012/040 | 6000-03/11A | 3960 | 0.10 | 1.60 | 0.02 | 0.008 | 0.15 | 0.02 | 0.06 | 90.00 | 0.12 | 0.09 | 0.10 | 0.15 | 0.02 |
- Grade specified in this table is produced within the conditions in the table as suitable for chemical and mechanical properties which are mentioned according to only relevant standard specification.
- The products are supplied in "thermomechanically rolled" condition.
- (Nb + V + Ti) ≤ 0.22%
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | Bend (Transverse , BMD) t: thickness | ||
|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||
| A801.8≤t≤2.99 | A53≤t≤20 | 180° | |||||
| MW GL-012/040 | 6000-03/11A | 3960 | 450-550 | 550-650 | 22 | 22 | Ø 0,5a |
- Tensile test values apply to "longitudinal" test pieces