3901 Quality Sheet Specification
Hot rolled steels for wheel manufacturing based on customer specification
AlternativesThere is no alternative to this sheet.
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Hot rolled steels for wheel manufacturing based on customer specification
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmin. | Cmax. | Mnmin. | Mnmax. | Pmax. | Smax. | Simax. | Almax. | |
|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||||
| MW | MW01 | 3901 | 0.025 | 0.13 | 0.15 | 0.575 | 0.02 | 0.02 | 0.05 | 0.05 |
- Grade specified in this table is produced within the conditions in the table as suitable for chemical and mechanical properties which are mentioned according to only relevant standard specification.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] t(thickness, mm) | A(%) min. t(thickness, mm) | Impact | ||||
|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||||
| 2≤t≤3 | 3.01≤t≤6 | A802≤t≤3 | A53.01≤t≤6 | Temperature ( ° C) | KVC J min. | ||||
| MW | MW01 | 3901 | 240-340 | 360-470 | 340-470 | 26 | 28 | 20 | 27 |
- The impact test is carried out only when specified at the time of enquiry and order and is not carried out for thickness thinner than 6 mm.
- Tensile test values apply to "transverse" test pieces