325 Quality Sheet Specification
Zinc coated (galvanized) low carbon steels for cold forming
AlternativesThere is no alternative to this sheet.
Flat / Galvanised
Galvanized flat steel is manufactured by zinc-coating both sides of cold rolled metal by hot-dipping process. After having coated the steel surface with zinc, the coating of the interface is transformed into an alloy of iron-zinc layer through heating by induction and the galvannealed steel is produced.
Zinc coated (galvanized) low carbon steels for cold forming
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmax. | Mnmax. | Pmax. | Smax. | Simax. | Almin. | Timax. | CEmax. | |
|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||||
| B53 3106 | XSG | 325 | 0.08 | 0.40 | 0.025 | 0.025 | 0.10 | 0.02 | 0.11 | 0.14 |
- "CE = C % + (Mn+Si)/6 %" formula applies for carbon equivalent.
- The Ti limit is specified as reference value according to Erdemir manufacturing practice. Other limits are customer specification limits.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] t(thickness, mm) | Rm [N/mm2] | A(%) min. | n90 | r90 | ||
|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||
| 0.4≤t≤1.47 | 1.48≤t≤2 | A80 | min. | |||||
| B53 3106 | XSG | 325 | 160-200 | 160-210 | 280-340 | 37 | 0.19 | 1.8 min. |
- Tensile test values apply to "transverse" test pieces
- Hardness is 50 HRB maximum.
- The mechanical properties are valid for a period of 6 months from the date on which the products are made available.