3701 Quality Sheet Specification
Medium-strength steels for shipbuilding
Reproducible Letter Symbols --> HRP --> HRPKK --> HRU --> HRUKK --> KRKK --> L --> LKK --> LP --> LPKK --> LR --> LRKK --> R --> RD --> RKK --> RP --> RPD --> RPKK --> TR --> TRK
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Medium-strength steels for shipbuilding
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmax. | Mnmin. | Pmax. | Smax. | Simax. | |
|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||
| ABS-P2-2022 | A | 3701 | 0.21 | 0.45 | 0.035 | 0.035 | 0.50 |
- C + (Mn/6) ≤ 0.40 %
- Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | ||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||||
| A2001.39≤t≤5 | A2005.01≤t≤10 | A20010.01≤t≤15 | A20015.01≤t≤20 | A20020.01≤t≤25 | A20025.01≤t≤26 | |||||
| ABS-P2-2022 | A | 3701 | 235 min. | 400-520 | 14 | 16 | 17 | 18 | 19 | 20 |
- Tensile test values apply to "transverse" test pieces
- Impact energy values for "full size" (10 X 10 mm) test specimens for thinner products, impact energy values decreases depending on the thickness.
- Impact test is not carried out for thickness thinner than 6 mm.
Flat / Plate
Heavy plate products are obtained by rolling semi-finished products with a rectangular cross-section (slab) produced by the continuous casting method to a specific temperature, with thicknesses ranging from 6.00 to 200.00 mm and widths ranging from 1000 to 3600 mm.
Medium-strength steels for shipbuilding
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmax. | Mnmin. | Pmax. | Smax. | Simax. | |
|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||
| ABS-P2-2022 | A | 3701 | 0.21 | 0.45 | 0.035 | 0.035 | 0.50 |
- C + (Mn/6) ≤ 0.40 %
- Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | Impact | ||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||||||||
| A2006≤t≤10 | A20010.01≤t≤15 | A20015.01≤t≤20 | A20020.01≤t≤25 | A20025.01≤t≤30 | A20030.01≤t≤40 | A20040.01≤t≤60 | Temperature ( ° C) | KVC J min. | |||||
| ABS-P2-2022 | A | 3701 | 235 min. | 400-520 | 16 | 17 | 18 | 19 | 20 | 21 | 22 | 20 | 34 |
- Tensile test values apply to "transverse" test pieces
- Impact energy values for "full size" (10 X 10 mm) test specimens for thinner products, impact energy values decreases depending on the thickness.
- Impact test is not carried out for thickness thinner than 6 mm.