6407 Quality Sheet Specification
Low-carbon unalloyed mild steels for cold reducing with the obligation of batch annealing
AlternativesThere is no alternative to this sheet.
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Low-carbon unalloyed mild steels for cold reducing with the obligation of batch annealing
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmin. | Cmax. | Mnmin. | Mnmax. | Pmin. | Pmax. | Smax. | Simax. | Almin. | Nbmin. | Nbmax. | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||||||||
| SAE J403-2014 | 1006 (MOD2) | 6407 | 0.02 | 0.08 | 0.15 | 0.45 | 0.01 | 0.025 | 0.025 | 0.04 | 0.02 | 0.002 | 0.015 |
- For the thickness of 2.80 mm, crown value is aimed between 30-40 micron.
- Mechanical test is not carried out.
- Mn, P and Nb values are requested as aiming.
- The limitation requests for the residual elements (Cu, Ni, Cr, Mo) which are not mentioned on the table are subjected to negotitation for special application purposes.
- Suitable for batch annealing after cold reducing.
- Deoxidation method of this products is fully-killed. Minimum aluminium to nitrogen ratio is 2:1.