6412 Quality Sheet Specification
Hot rolled low strength steels suitable for continuous annealing after cold reducing
Reproducible Letter Symbols --> BCKK --> HCKK --> TCK
AlternativesThere is no alternative to this sheet.
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Hot rolled low strength steels suitable for continuous annealing after cold reducing
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmax. | Mnmax. | Pmax. | Smax. | Simax. | Almin. | Nmax. | |
|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||||
| DIN 1614-1:1986 | St22 | 6412 | 0.08 | 0.40 | 0.025 | 0.025 | 0.03 | 0.02 | 70.00 |
- Cu + Ni + Cr + Mo ≤ 0.25 %
- The maximum value for nitrogen does not apply if the chemical composition shows a minimum total aluminium content of 0.020%.
- Mechanical test is not carried out.
- Suitable for continous annealing after cold reducing.
- Al value specified in the table is the aimed value.