713 Quality Sheet Specification
Hot rolled steels for deep-drawing and cold forming
AlternativesThere is no alternative to this sheet.
Flat / Hot Rolled
Flat steel products are obtained by heating semi-finished products with a rectangular cross-section (slab), which are produced by the continuous casting method, to a specific temperature and then rolling them, with thicknesses ranging from 1.40 to 25.40 mm and widths ranging from 700 to 2025 mm, produceed as coil or by cutting/slit-coiling flat steel products from coils.
Hot rolled steels for deep-drawing and cold forming
Chemical Composition (%)
| Standard Equivalent | Erdemir Grade No | Cmin. | Cmax. | Mnmin. | Mnmax. | Pmax. | Smax. | Al+Simin. | Al+Simax. | |
|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Quality | |||||||||
| 400-040-101 | VAW HRC1/HRC3 | 713 | 0.02 | 0.08 | 0.15 | 0.50 | 0.03 | 0.03 | 0.01 | 0.11 |
- The ratio of Al% + Si% is between 0.01-0.11
- Grade specified on the table, is produced within the framework of agreements with customers.
Mechanical Properties
| Standard Equivalent | Erdemir Grade No | Re [N/mm2] | Rm [N/mm2] | A(%) min. t(thickness, mm) | |||
|---|---|---|---|---|---|---|---|
| Standard | Quality | ||||||
| A801.5≤t≤2 | A802.01≤t≤2.99 | A53≤t≤5 | |||||
| 400-040-101 | VAW HRC1/HRC3 | 713 | 170 min. | 270-400 | 28 | 29 | 33 |
- Tensile test values apply to "transverse" test pieces